Assessment of NiO-CGO composites as cermet precursors

作者：Grilo Joao P F; Macedo Daniel A; Nascimento Rubens M; Marques Fernando M B^*

来源：Solid State Ionics, 2018, 321: 115-121.

DOI：10.1016/j.ssi.2018.04.014

• One-step synthesis
• Composites
• Cermets
• Microstructure
• Electrical properties

NiO-Ce0.9Gd0.1O1.95 (NiO-CGO) composite powders produced by a one-step chemical route were assessed as precursors of fuel cell anode cermets. Porous NiO-CGO composites were prepared by uniaxial pressing followed by firing at 1400 degrees C for 4 h. Ni-CGO cermets were subsequently obtained by reduction in 10 vol% H-2 + 90 vol% N-2 at 750 degrees C. Similar materials obtained by conventional mechanical mixing of commercial powders were also prepared and tested. The structure and particle size of the calcined material were investigated by X-ray diffraction (XRD) and Transmission Electron Microscopy (TEM). The electrical properties of all materials were duly studied by impedance spectroscopy (NiO-CGO) (in air and several N-2 + O-2 gas mixtures) or dc conductivity (Ni-CGO). The total and relative magnitude of impedance arcs observed in the low temperature impedance spectra can be used to obtain significant insight on microstructural characteristics, due to a variable role of NiO when shifting from a well percolated electronic conducting pathway to a dispersed ion-blocking phase. The confirmed superior conductivity of one-step materials was interpreted as a consequence of the presence of a network of well-connected and homogeneously distributed NiO(/Ni) grains, as shown by SEM.

• 出版日期2018-8