Competitive twinning behavior in magnesium and its impact on recrystallization and texture formation

作者：Basu I^*; Al Samman T

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2017, 707: 232-244.

DOI：10.1016/j.msea.2017.09.053

• Texture
• Dynamic recovery
• Recrystallization
• Magnesium
• Rare-earths

Rolled pure Mg and Mg-1 wt% Gd alloy were subjected to room temperature in-plane compression along the rolling direction, followed by isochronal annealing treatments for 1 h. The results of deformation texture and microstructure showed substantial differences due to rare earth alloying. In spite of imposed c-axis extension during deformation, the Mg-1Gd alloy retained the initial texture with the majority of basal poles concentrated near the longitudinal direction of the used channel-die tool. Electron back scatter diffraction analysis of the deformation microstructure revealed a predominance of {10 (1) over bar1} compression and {10 (1) over bar1}-{10 (1) over bar2} double twins relative to coexisting {10 (1) over bar2} tension twins. This behavior was significantly contrasting in comparison with that of pure Mg, wherein first and second generation {1012} tension twins were observed in profuse quantities. Continuous dynamic recrystallization took place inside compression and double twins by means of slip assisted subgrain rotation about the [0001] axis giving rise to a sharp prismatic fiber of recrystallized orientations. This fiber was transformed into a randomized texture pattern during subsequent static recrystallization and grain growth due to a different discontinuous recrystallization mechanism. This resulted in a significant annealing texture weakening and an increase of the overall Schmid factor for basal slip.

• 出版日期2017-11-7