Mode I Fracture Toughness of CNT-Reinforced PMMA

作者：Simhi T^*; Banks Sills L; Fourman V; Shlayer A

来源：STRAIN, 2015, 51(6): 474-482.

DOI：10.1111/str.12158

• CNTs
• fracture toughness
• nano-reinforcement
• PMMA
• stress concentration factor

The influence of carbon nanotube ( CNT) concentration on the fracture toughness of poly( methyl methacrylate) ( PMMA) was examined on single- edge V- notched- beam ( SEVNB) specimens. Six groups of SEVNB specimens containing 0.5, 1, 2, 4, 8.5 wt% of CNTs and neat PMMA as a reference were tested. First, a notch was introduced into the specimens by a specially made disk whose edge is V- shaped with a 30 mu angle and a 30 mu m tip width. As suggested by an American Society for Testing and Materials Standard for polymers, induction of a natural crack was attempted, without success. Therefore, fracture toughness values were determined with the `sharp' machined notch by means of a calibration formula. These were compared to values obtained using a stress concentration factor and found to differ by less than 3%. The latter calculation takes into account the geometry of the notch. Results showed a decrease in the fracture toughness values with an increase in the CNT concentration. For specimens in which a natural crack was attempted, referred to as a razor- cut notch, a significant increase in the apparent fracture toughness was observed, as a result of the induced damage.

• 出版日期2015-12