Post-combustion CO2 capture by formic acid-modified CaO-based sorbents

作者：Ridha Firas N; Manovic Vasilije; Wu Yinghai; Macchi Arturo; Anthony Edward J^*

来源：International Journal of Greenhouse Gas Control, 2013, 16: 21-28.

DOI：10.1016/j.ijggc.2013.02.026

• CO2 capture
• CaO-based sorbent
• Formic acid
• Post-combustion
• Calcium looping

The performance of CaO-based sorbents modified with formic acid in both its liquid and vapor phase has been investigated for high-temperature post-combustion CO2 capture in calcium-looping cycles. The treatment of limestone with aqueous solutions containing 10 or 30 vol% formic acid was found to promote crystal growth. By contrast, higher acid concentrations produced smaller crystals. However, all sorbents modified by acid solutions had almost identical reductions of 44% and 46% in surface area and pore volume (determined by N-2 adsorption), respectively, relative to the parent material. Despite the low porosity, limestone (fine powder) treated with 10% acid solution displayed the highest CO2 capture capacity in the first cycle with a capture of 0.6 g CO2/g sorbent compared to 0.49 g/g for untreated powder material. By 20 cycles, the modified sorbent still captured 67.4% more CO2 than the natural sorbent captured under similar conditions. Relatively low concentration formic acid solution improved the CO2 capture capacity of CaO-based sorbents better than treatment with acid vapor due to the limited acidification achieved by vapor phase treatment.

• 出版日期2013-8