Lithium bis(oxalato)borate as an electrolyte for micromesoporous carbide-derived carbon based supercapacitors

作者：Laheaeaer Ann; Jaenes Alar; Lust Enn^*

来源：Journal of Electroanalytical Chemistry, 2012, 669: 67-72.

DOI：10.1016/j.jelechem.2012.01.025

• Supercapacitor
• Carbide-derived carbon
• LiBOB electrolyte
• Carbonate solvents

1 M solution of lithium bis(oxalato)borate (LiBOB) in ethylene carbonate (EC) and dimethyl carbonate (DMC) mixture (1:1 volume ratio) was studied as an electrolyte for supercapacitors with high surface area micromesoporous carbide-derived carbon electrodes, synthesized from MO2C. Electrochemical characteristics were studied using cyclic voltammetry, electrochemical impedance spectroscopy (EIS) and constant current charge/discharge methods. The established region of ideal polarizability for a two-electrode system was similar to 3.0 V and the limiting capacitance, calculated from EIS data, was 125 F g(-1). Three-electrode measurements showed that solid electrolyte interface formation is a very complex process and partially blocks the adsorption and intercalation/deintercalation processes on the negatively charged electrode. The capacitance of a supercapacitor cell decreased by 33% during 5000 galvanic cycles between applied cell voltages from 1.5 V to 3.0 V. Calculated maximal energy and power densities were 42.5W h kg(-1) and 67.3 kW kg(-1), respectively. Thus, the tested LiBOB electrolyte is a potential candidate for long-lasting supercapacitors with high power density.

• 出版日期2012-3-15