Use of Microencapsulated Phase-Change Materials To Regulate the Temperature of Oilwell Cement

作者：Pang Xueyu^*; Jimenez Walmy Cuello; Goel Vivek

来源：SPE DRILLING & COMPLETION, 2016, 31(1): 063-070.

DOI：10.2118/171769-pa

• Cement based composite material
• Cementing operations
• Isothermal calorimetry
• Long-term integrity
• Low young's modulus
• Microencapsulated phase change material
• Strength development
• Supplementary cementitious material

During the cementing operations of oil wells, there are many situations in which it is crucial to regulate the temperature of the cement slurry during and after its placement. Limiting the temperature rise of cement-based composite materials was traditionally achieved by reducing the heat of hydration of the composite (e.g., through the use of supplementary cementitious materials or inert filling materials). However, the total amount of heat generated by a cement composite is primarily determined by the hydration extent of the cement that has a strong correlation with the composite's strength development. Reducing the heat of hydration of oilwell cement through chemical means typically results in lower strength of the material, especially during early ages.
This study investigates the application of a novel material-namely, microencapsulated phase-change material (MPCM)-to regulate the temperature of oilwell cement with a physical method. The MPCM acts as an energy-storage medium that absorbs heat when the temperature of the cement reaches the melting point of the phase-change material (PCM), and releases heat when the temperature drops below its freezing/crystallization point. The solid polymer shell that encapsulates the PCM prevents the melted material from chemically interacting with the cement matrix. Hence, the strength development of the cement matrix is largely unaffected. Moreover, the set cement composite appears to be more elastic and less brittle because of the addition of the MPCM, which is beneficial to the long-term integrity of the cement.
During this study, the heat evolution of cement slurries was investigated by both isothermal calorimetry and semiadiabatic tests. A similar amount of heat was generated by most slurries, as shown by isothermal calorimetry tests. However, results from semiadiabatic tests and compressive-strength tests show that the slurry prepared with MPCM in a solid state exhibited least temperature rise and optimal mechanical properties (high strength and high-strain capacity), which can be attributed to desirable properties of the PCM including high latent heat and low Young's modulus.

• 出版日期2016-3