Size controlled synthesis of sub-100 nm monodisperse poly(methylmethacrylate) nanoparticles using surfactant-free emulsion polymerization

作者：Camli Sevket Tolga^*; Buyukserin Fatih; Balci Oguz; Budak Gurer Guven

来源：Journal of Colloid and Interface Science, 2010, 344(2): 528-532.

DOI：10.1016/j.jcis.2010.01.041

• Poly(methylmethacrylate)
• Nanoparticles
• Surfactant-free emulsion polymerization
• Monodisperse
• Dynamic light scattering

Surfactant-free emulsion polymerization (SFEP) is a well-known technique for the production of polymeric nanoparticles that does not require post-synthetic cleaning steps. Obtaining hydrophobic particles at sub-100 nm scale, however, is quite challenging with this polymerization method. Here, we demonstrate a single step synthetic approach that yields poly(methyl methacrylate) (PMMA) nanoparticles with controlled sub-100 nm size and relatively high resultant solid content. Dynamic light scattering (DLS) was used for the particle characterization. Spherical and uniformly sized nanoparticles were confirmed by atomic force microscopy (AFM) and scanning electron microscopy (SEM). Acetone was used as a cosolvent in order to obtain monodisperse sub-100 nm diameter particles. Stable PMMA nanoparticle dispersions were obtained for all formulations where the persulfate initiator causes the negative charges on the particle surface. The effects of acetone, monomer and initiator concentration were studied to optimize average particle hydrodynamic diameter and polydispersity index of the final particles. Non-crosslinked monodisperse PMMA nanoparticles (polydispersity index less than 0.05) with diameters from 32 nm to 72 nm were synthesized by using this method.

• 出版日期2010-4-15