In this study, the effects of partial Sb3+ ion substitutions for the Y sites and the Cu sites on the superconducting properties of YBa2Cu3O (y) (Y123) ceramic superconductors were investigated. The samples were prepared by the conventional solid-state reaction method and the properties of the samples were investigated by means of X-ray diffraction, AC magnetic susceptibility measurements, scanning electron microscope, and energy dispersive X-ray analysis. The critical temperatures were determined to be in the range of 80-92 K for both Systems I and II. It was found that Sb-addition leads to the formation of the non-superconducting YBa2SbO6 phase, which has a negative effect on the critical temperature, since the highest critical temperature was measured for pure Y123. However, the increasing substitution level has a negligible effect on the X-ray diffraction analysis peak intensities of the superconducting phases. In addition, SEM images showed that Sb substitution decreases the grain size and modifies the microstructure development, which makes the samples denser.
- 出版日期2011-11