Change of phase composition and morphology of sonochemically synthesised hydroxyapatite nanoparticles with glycosaminoglycans during thermal treatment

作者：Han, Y. C.^*; Wang, X. Y.; Li, S. P.

来源：Advances in Applied Ceramics, 2009, 108(7): 400-405.

DOI：10.1179/174367609X414134

• Hydroxyapatite
• Nanoparticles
• Sonochemical synthesis
• Glycosaminoglycans
• Thermal treatment
• Glass ceramic powders

Based on the preparation of glycosaminoglycans (GAGs) stabilised hydroxyapatite (HAP) nanoparticle suspension via sonochemical synthesis, the change of phase composition and morphology of freeze dried HAP nanoparticles with GAGs was investigated from 500 to 1200 degrees C by TEM, X-ray diffraction, Fourier transform infrared spectroscopy and SEM. Results show that thermal treatment brought the phase transformation and the morphology change of HAP nanoparticles. In the low temperature stage (similar to 650 degrees C), the samples were mainly composed of HAP as main crystalline phase and beta-NaCaPO(4) as minor crystalline phase. This phase transformation was mainly attributed to the residues containing sodium derived from combustion of GAGs. The particles were near spherical, and the nanocrystalline nature was retained. In the high temperature stage (650-1200 degrees C), the samples were glass ceramic powders composed of HAP, beta-tricalcium phosphate, Na(3)Ca(6)(PO(4))(5), beta-NaCaPO(4) and Na-Ca-P-O glass phase. The grains rapidly grew into larger particles with morphology transformation from rodlike shape to irregular shape and the size increase from (0.1-0.15) x (0.3-0.5) mu m to 1.5-10 mu m.

• 出版日期2009-10
• 单位武汉理工大学