(Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high-entropy ceramics with low thermal conductivity

作者：Yan, Xueliang; Constantin, Loic; Lu, Yongfeng; Silvain, Jean-Francois; Nastasi, Michael; Cui, Bai^*

来源：Journal of the American Ceramic Society, 2018, 101(10): 4486-4491.

DOI：10.1111/jace.15779

• high-entropy ceramics
• microstructure
• spark plasma sintering
• thermal conductivity

A novel high-entropy carbide ceramic, (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C, with a single-phase rock salt structure, was synthesized by spark plasma sintering. X-ray diffraction confirmed the formation of a single-phase rock salt structure at 26-1140 degrees C in Argon atmosphere, in which the 5 metal elements may share a cation position while the C element occupies the anion position. (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C exhibits a much lower thermal diffusivity and conductivity than the binary carbides HfC, ZrC, TaC, and TiC, which may result from the significant phonon scattering at its distorted anion sublattice. (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C inherits the high elastic modulus and hardness of the binary carbide ceramics.

• 出版日期2018-10