Mechanical properties at room temperature of an Al-Zn-Mg-Cu alloy processed by equal channel angular pressing

作者：Cepeda Jimenez C M^*; Garcia Infanta J M; Ruano O A; Carreno F

来源：Journal of Alloys and Compounds, 2011, 509(35): 8649-8656.

DOI：10.1016/j.jallcom.2011.06.070

• Al-Zn-Mg-Cu alloy
• Severe plastic deformation
• ECAP
• Microstructure
• Mechanical properties

Tensile tests were conducted to evaluate the influence of equal-channel angular pressing (ECAP) on the mechanical properties at room temperature of overaged Al 7075-O alloy. ECAP processing was performed using route B-C at different temperatures and number of passes, i.e. different processing severity conditions. The maximum load (F-max) recorded during the last pass of each ECAP path considered in this study is a very good estimation of the processing severity. The mechanical properties were studied in terms of the balance between tensile strength and ductility. In the processed Al 7075-O alloy, the grain size was reduced down to similar to 150 nm. Consequently, tensile testing at room temperature revealed a significant increase in the maximum tensile strength after ECAP with respect to the as start material. In the present study, as the processing severity increases with the number of ECAP passes or with the decrease in processing temperature, there is a consistent trend of increment in ultimate tensile strength with minor decrease in uniform plastic elongation respect to the first ECAP pass at room temperature. This is in contrast to the behaviour after more severe plastic deformation conditions, where an increase in strength together with a strong decrease in elongation would be expected.

• 出版日期2011-9-1