NiO Nanoparticles Anchored on Phosphorus-Doped -Fe2O3 Nanoarrays: An Efficient Hole Extraction p-n Heterojunction Photoanode for Water Oxidation

作者：Li, Feng; Li, Jing; Zhang, Jie; Gao, Lili; Long, Xuefeng; Hu, Yiping; Li, Shuwen; Jin, Jun^*; Ma, Jiantai^*

来源：Chemsuschem, 2018, 11(13): 2156-2164.

DOI：10.1002/cssc.201800571

• doping
• electrochemistry
• nanostructures
• photochemistry
• water splitting

The photoelectrochemical (PEC) water-splitting efficiency of a hematite-based photoanode is still far from the theoretical value due to its poor surface reaction kinetics and high density of surface trapping states. To solve these drawbacks, a photoanode consisting of NiO nanoparticles anchored on a gradient phosphorus-doped -Fe2O3 nanorod (NR) array (NiO/P--Fe2O3) was fabricated to achieve optimal light absorption and charge separation, as well as rapid surface reaction kinetics. Specifically, a photoanode with the NR array structure allowed a high mass-transport rate to be achieved, while phosphorus doping effectively decreased the number of surface trapping sites and improved the electrical conductivity of -Fe2O3. Furthermore, the p-n junction that forms between NiO and P--Fe2O3 can further improve the PEC performance due to efficient hole extraction and the water oxidization catalytic activity of NiO. Consequently, the NiO/P--Fe2O3 NR photoanode produced a high photocurrent density of 2.08mAcm(-2) at 1.23V versus a reversible hydrogen electrode and a 110mV cathodic shift of the onset potential. This rational design of structure offers a new perspective in exploring high-performance PEC photoanodes.

• 出版日期2018-7-11
• 单位兰州大学