The densification behavior of 20-40-nm graphite-coated B,C nano-particles was studied using dilatometry, x-ray diffraction, and electron microscopy. The sintering onset temperature was higher than expected from a nanoscale powder (similar to 1500 degrees C); remnant B2O3 kept particles separated until B2O3 volatilization, and the graphite coatings imposed particle-to-particle contact of a substance more refractory than B4C. Solid-state sintering (1500-1850 degrees C was followed by a substantial slowing of contraction rate attributed to the formation of eutectic liquid droplets more than 10x the size of the original nano-particles. These droplets were induced to form well below the B,C-graphite eutectic temperature by the high surface energy of nanoparticles. They were interpreted to have quickly solidified to form a vast number of voids in particle packing, which in turn, impeded detection of continued solid-state sintering. Starting at 2200 degrees C, a permanent and interconnected liquid phase formed, which facilitated rapid contraction by liquid phase sintering and/or compact slumping.
- 出版日期2007-5