Nanostructural Free-Volume Effects in Humidity-Sensitive MgO-Al2O3 Ceramics for Sensor Applications

作者：Klym H; Ingram A; Shpotyuk O; Hadzaman I; Hotra O; Kostiv Yu

来源：Journal of Materials Engineering and Performance, 2016, 25(3): 866-873.

DOI：10.1007/s11665-016-1931-9

• ceramics
• electron microscopy
• microporous materials
• microstructure
• positron annihilation spectroscopy

Technologically modified spinel MgO-Al2O3 ceramics were prepared from Al2O3 and 4MgCO(3)center dot Mg(OH)(2)center dot 5H(2)O powders at sintering temperatures of 1200, 1300, and 1400 A degrees C. Free-volume structural effects in MgO-Al2O3 ceramics and their electrophysical properties were studied using combined x-ray diffraction, scanning electron microscopy, Hg-porosimetry, and positron annihilation lifetime spectroscopy. It is shown that increasing of sintering temperature from 1200 to 1400 A degrees C results in the transformation of pore size distribution in ceramics from tri- to bi-modal including open macro- and meso(micro)pores with sizes from ten to hundreds nm and nanopores with sizes up to a few nm. Microstructure of these ceramics is improved with the increase of sintering temperature, which results in decreased amount of additional phases located near grain boundaries. These phase extractions serve as specific trapping centers for positrons penetrating the ceramics. The positron trapping and ortho-positronium decaying components are considered in the mathematical treatment of the measured spectra. Classic Tao-Eldrup model is used to draw the correlation between the ortho-positronium lifetime and the size of nanopores, which is complementary to porosimetry data. The studied ceramics with optimal nanoporous structure are highly sensitive to humidity changes in the region of 31-96% with minimal hysteresis in adsorption-desorption cycles.

• 出版日期2016-3