Comparative study on twinning characteristics during two post-weld compression paths and their effects on joint enhancement

作者：Liu, Zhe; Xin, Renlong^*; Li, Dongrong; Sun, Liyun; Liu, Qing^*

来源：Scientific Reports, 2016, 6(1): 39779.

DOI：10.1038/srep39779

• FRICTION STIR WELD
• MAGNESIUM ALLOY
• MECHANICAL-PROPERTIES
• TENSILE BEHAVIOR
• GRAIN-SIZE
• DEFORMATION-BEHAVIOR
• TEXTURE DEVELOPMENT
• FRACTURE-BEHAVIOR
• MG ALLOYS
• MICROSTRUCTURE

Friction stir welding (FSW) has promising application potential in Mg alloys. However, the texture distribution in stir zone (SZ) is usually complicated for Mg alloys, which deterioriates the joint performance. In this study, the texture distribution in SZ was tailored by applying two kinds of post-weld compression deformation along normal direction (ND) or welding direction (WD) of the FSWed AZ31 Mg alloy plates. The twinning behavior and texture change in the various regions of SZ were then evaluated by electron back scatter diffraction (EBSD) characterization. The effect of texture change on the joint performance was discussed in terms of Schmid factors (SFs) for basal slip and extension twinning. The results showed that profuse extension twins were formed through the whole SZ for the sample subjected to compression along ND, whereas they were observed mainly in SZ-side for the sample compressed along WD. Most of the twins were present in the forms of twin bands or chains. The directions of the twin bands or chains were related to the habit plane traces of selected twin variants. The ND post-weld compression had better strengthening effects on the joints compared to the WD compression, and the underline mechanism was discussed.

• 出版日期2016-12-23
• 单位重庆大学