Advantages of using amorphous indium zinc oxide films for window layer in Cu(In,Ga)Se-2 solar cells

作者：Warasawa, Moe; Kaijo, Akira; Sugiyama, Mutsumi^*

来源：Thin Solid Films, 2012, 520(6): 2119-2122.

DOI：10.1016/j.tsf.2011.08.093

• Indium zinc oxide
• Transparent conducting oxide
• Window layer
• Copper indicum gallium selenide
• Solar cells
• Sputtering

The advantages of using indium zinc oxide (IZO) films instead of conventional Ga-doped zinc oxide (ZnO:Ga) films for Cu(In,Ga)Se-2 (CIGS) solar cells are described. The electrical properties of IZO are independent of film thickness. IZO films have higher mobility (30-40 cm(2)/Vs) and lower resistivity (4-5 x 10(-4) Omega cm) compared to ZnO:Ga films deposited without intentional heating, because the number of grain boundaries in amorphous IZO films is small. The properties of a CIGS solar cell using IZO at the window layer were better than those obtained using a conventional ZnO:Ga at the window layer; moreover, the properties tended to be independent of thickness. These results indicate that use of IZO as a transparent conducting oxide layer is expected to increase the efficiency of CIGS solar cells.

• 出版日期2012-1-1