The microstructure and phase composition of low-pressure die-cast (LPDC) and high-pressure die-cast (HPDC) magnesium alloy AM50 were examined by transmission electron microscopy (TEM) techniques in combination with optical microscopy, scanning electron microscopy (SEM), and electron-probe microanalysis (EPMA). It has been established that the dimensions and morphology of the constituent phases (alpha-Mg solid solution, Mg17Al12, and Al8Mn5) depend on the processing parameters. The results obtained suggest that there is a ternary eutectic with the aforementioned three phases in the Mg-Al-Mn system. Phase transformations leading to the observed microstructures are discussed.