A facile route to synthesis of S-doped TiO2 nanoparticles for photocatalytic activity

作者：McManamon Colm^*; O'Connell John; Delaney Paul; Rasappa Sozaraj; Holmes Justin D; Morris Michael A

来源：Journal of Molecular Catalysis A: Chemical , 2015, 406: 51-57.

DOI：10.1016/j.molcata.2015.05.002

• TiO2
• S-doped
• Band gap
• Photocatalysis

There is always a market for cost effective methods of pollution degradation and one of the best areas to keep costs down is through synthesis techniques. This paper provides a simple technique to synthesise porous TiO2 nanoparticles with increased surface area through a scaffold template technique. Their photocatalytic activity is enhanced by incorporating sulphur as a dopant and were validated by analysing the degradation of malachite green (MG). The materials were doped at a molar ratio of 100:1 (Ti:S) and calcined at different temperatures to adjust the anatase/rutile content. Detailed characterisation of the materials was undertaken using XRD, BET, XPS, TEM and FTIR. The nanoparticles displayed a microporous structure and had an increased surface area of 115 m(2) g(-1) which was reduced by doping and temperature induced phase transformation. Photocatalytic testing showed that the doped materials calcined at 700 degrees C preformed the best in. It was observed that 20 mgl(-1) of MG was decomposed in 30 min using a 40W UV bulb at pH 9 and the results surpassed those achieved by the commercial catalyst P25 which was also tested for comparison.

• 出版日期2015-9