Low cytotoxic tissue adhesive based on oxidized dextran and epsilon-poly-L-lysine

作者：Hyon Suong Hyu^*; Nakajima Naoki; Sugai Hajime; Matsumura Kazuaki

来源：Journal of Biomedical Materials Research Part A, 2014, 102(8): 2511-2520.

DOI：10.1002/jbm.a.34923

• dextran
• periodate
• epsilon-poly(L-lysine)
• adhesive
• cytotoxicity

A novel adhesive hydrogel consisting of dextran and epsilon-poly(L-lysine) (dextran-PL) with multiple biomedical applications was developed. Periodate oxidation in aqueous media almost stoichiometrically introduces aldehyde groups in dextran molecules, and aldehyde dextran can react with the primary amino groups in epsilon-PL (epsilon-PL) at neutral pH to form a hydrogel. The gelation time of the hydrogel can be easily controlled by the extent of oxidation in dextran and of the acylation in epsilon-PL by anhydrides. The shear adhesion strength of dextran-PL was 10 times higher than that of fibrin glue, when wet collagen sheets were selected as test specimens. The cytotoxicity of aldehyde dextran and epsilon-PL were 1000 times lower than that of glutaraldehyde and poly(allylamine). The considerably low cytotoxicity of aldehyde dextran could be ascribed to its low reactivity with amine species when compared with glutaraldehyde. In contrast, a high reactivity of amino groups in epsilon-PL was observed when compared with glycine, L-lysine, and gelatin, which could be explained by their poor dissociation at neutral pH, thus leading to low cytotoxicity.

• 出版日期2014-8