Delamination detection and impact damage assessment of GLARE by active thermography

作者：Ibarra Castanedo Clemente; Avdelidis Nicolas P^*; Grinzato Ermanno G; Bison Paolo G; Marinetti Sergio; Plescanu Claudiu Cochior; Bendada Abdelhakim; Maldague Xavier P

来源：International Journal of Materials and Product Technology, 2011, 41(1-4): 5-16.

DOI：10.1504/ijmpt.2011.040282

• active thermography
• GLARE composites
• fibre metal laminates
• FMLs
• pulsed thermography
• PT
• vibrothermography
• VT
• C-scan ultrasounds
• impact damage
• delaminations

GLAss REinforced (GLARE) is a fibre metal laminate (FML) consisting of alternating layers of thin aluminium and glass fibre reinforced prepregs, whose improved physical properties confer it an interesting advantage over aluminium and composite materials for a number of aerospace applications. On the other hand, contrary to monolithic structures, GLARE can suffer from internal damage either during fabrication or in-serve stages. Non-destructive testing and evaluation (NDT&E) of GLARE is still a challenge, especially considering that large structures are typically sought (e.g., aircraft fuselage). In this paper, we investigated the use of infrared thermography for the inspection of GLARE. The experimental results presented herein demonstrate that it is possible to detect delamination-type defects and to assess the impact severity on GLARE through active thermography techniques, specifically pulsed thermography and vibrothermography. C-scan ultrasonic testing was performed as well with the intention of providing supplementary results.