An inset CT specimen for evaluating fracture in small samples of material

作者:Yahyazadehfar M; Nazari A; Kruzic J J; Quinn G D; Arola D*
来源:Journal of the Mechanical Behavior of Biomedical Materials, 2014, 30: 358-368.
DOI:10.1016/j.jmbbm.2013.10.017

摘要

In evaluations on the fracture behavior of hard tissues and many biomaterials, the volume of material available to study is not always sufficient to apply a standard method of practice. In the present study an inset Compact Tension (inset CT) specimen is described, which uses a small cube of material (approximately 2 x 2 x 2 mm(3)) that is molded within a secondary material to form the compact tension geometry. A generalized equation describing the Mode I stress intensity was developed for the specimen using the solutions from a finite element model that was defined over permissible crack lengths, variations in specimen geometry, and a range in elastic properties of the inset and mold materials. A validation of the generalized equation was performed using estimates for the fracture toughness of a commercial dental composite via the %26quot;inset CT%26quot; specimen and the standard geometry defined by ASTM E399 (2006). Results showed that the average fracture toughness obtained from the new specimen (1.23 +/- 0.02 MPa m(0.5)) was within 2% of that from the standard. Applications of the inset CT specimen are presented for experimental evaluations on the crack growth resistance of dental enamel and root dentin, including their fracture resistance curves. Potential errors in adopting this specimen are then discussed, including the effects of debonding between the inset and molding material on the estimated stress intensity distribution. Results of the investigation show that the inset CT specimen offers a viable approach for studying the fracture behavior of small volumes of structural materials.

  • 出版日期2014-2