Microstructure and high-temperature tribological properties of Si-doped hydrogenated diamond-like carbon films

作者：Zhang, Teng Fei; Wan, Zhi Xin; Ding, Ji Cheng; Zhang, Shihong; Wang, Qi Min; Kim, Kwang Ho^*

来源：Applied Surface Science, 2018, 435: 963-973.

DOI：10.1016/j.apsusc.2017.11.194

• Si-doped DLC films
• Microstructure
• Hardness
• High-temperature tribology
• Wear
• HiPIMS

Si-doped DLC films have attracted great attention for use in tribological applications. However, their high-temperature tribological properties remain less investigated, especially in harsh oxidative working conditions. In this study, Si-doped hydrogenated DLC films with various Si content were synthesized and the effects of the addition of Si on the microstructural, mechanical and high-temperature tribological properties of the films were investigated. The results indicate that Si doping leads to an obvious increase in the sp(3)/sp(2) ratio of DLC films, likely due to the silicon atoms preferentially substitute the sp(2)-hybridized carbon atoms and augment the number of sp(3) sites. With Si doping, the mechanical properties, including hardness and adhesion strength, were improved, while the residual stress of the DLC films was reduced. The addition of Si leads to higher thermal and mechanical stability of DLC films because the Si atoms inhibit the graphitization of the films at an elevated temperature. Better high-temperature tribological properties of the Si-DLC films under oxidative conditions were observed, which can be attributed to the enhanced thermal stability and formation of a Si-containing lubricant layer on the surfaces of the wear tracks. The nano-wear resistance of the DLC films was also improved by Si doping.

• 出版日期2018-3-30
• 单位广东工业大学; 安徽工业大学