Determination of proton- and oxide ion tracer diffusion in lanthanum tungstate (La/W=5.6) by means of ToF-SIMS

作者：Hancke Ragnhild; Fearn Sarah; Kilner John A; Haugsrud Reidar^*

来源：Physical Chemistry Chemical Physics, 2012, 14(40): 13971-13978.

DOI：10.1039/c2cp42278f

Tracer diffusion of protons and oxide ions, as well as chemical diffusion of water, have been determined for the high temperature proton conductor lanthanum tungstate by means of time-of-flight secondary ion mass spectrometry (ToF-SIMS). The oxygen tracer diffusion and surface exchange coefficients, D*(O) and k*(O), were measured after exchange anneals in water vapor enriched in (H2O)-O-18 between 350 and 620 degrees C, and the apparent activation energies were 176 and 82 kJ mol(-1), respectively. The hydrogen tracer diffusion coefficient (D*(H)) was measured between 220 and 320 degrees C after exchange anneals in D2O-containing atmospheres, and the apparent activation energy was 63 kJ mol(-1). The extracted D*(H) agrees with the results of transient conductivity-and TG-measurements. Chemical diffusion and surface exchange coefficients, D-H(delta) and k(H)(delta), were measured at 250 and 400 degrees C, and the result confirms that the material is hydrated by ambipolar sluggish transport of protons and oxide ions. The surface exchange coefficients were compared to the result of TG relaxation, suggesting that access to oxygen vacancies limits the overall surface exchange reaction under incorporation of water and oxygen.

• 出版日期2012