Nano-sized Mo- and Nb-doped TiO2 as anode materials for high energy and high power hybrid Li-ion capacitors

作者：Bauer Dustin; Roberts Alexander J; Matsumi Noriyoshi; Darr Jawwad A^*

来源：Nanotechnology, 2017, 28(19): 195403.

DOI：10.1088/1361-6528/aa69df

• continuous hydrothermal flow synthesis
• doped anatase
• hybrid Li-ion capacitor

Nano-sized Mo-doped titania (Mo0.1Ti0.9O2) and Nb-doped titania (Nb0.25Ti0.75O2) were directly synthesized via a continuous hydrothermal flow synthesis process. Materials characterization was conducted using physical techniques such as transmission electron microscopy, powder x-ray diffraction, x-ray photoelectron spectroscopy, Brunauer-Emmett-Teller specific surface area measurements and energy dispersive x-ray spectroscopy. Hybrid Li-ion supercapacitors were made with either a Mo-doped or Nb-doped TiO2 negative electrode material and an activated carbon (AC) positive electrode. Cells were evaluated using electrochemical testing (cyclic voltammetry, constant charge discharge cycling). The hybrid Li-ion capacitors showed good energy densities at moderate power densities. When cycled in the potential window 0.5-3.0 V, the Mo0.1Ti0.9O2/AC hybrid supercapacitor showed the highest energy densities of 51 Wh kg(-1) at a power of 180 W kg(-1) with energy densities rapidly declining with increasing applied specific current. In comparison, the Nb0.25Ti0.75O2/AC hybrid supercapacitor maintained its energy density of 45 Wh kg(-1) at 180 W kg(-1) better, showing 36 Wh g(-1) at 3200W kg(-1), which is a very promising mix of high energy and power densities. Reducing the voltage window to the range 1.0-3.0 V led to an increase in power density, with the Mo0.1Ti0.9O2/AC hybrid supercapacitor giving energy densities of 12 Wh kg(-1) and 2.5 Wh kg(-1) at power densities of 6700 W kg(-1) and 14 000W kg(-1), respectively.

• 出版日期2017-5-12