Miscibility and Isothermal Crystallization Behavior of Poly (Butylene Succinate-co-Adipate) (PBSA)/Poly (Trimethylene Carbonate) (PTMC) Blends

作者：Zhao, Lifen^*; Tian, Xiujuan; Liu, Xin; He, Haifeng; Zhang, Jun; Zhang, Ruliang^*

来源：Journal of Macromolecular Science Part B-Physics, 2016, 55(6): 591-604.

DOI：10.1080/00222348.2016.1179163

• crystallization kinetics
• equilibrium melting point
• glass transition temperatures
• miscibility
• poly(butylene succinate-co-adipate)
• poly(trimethylene carbonate)

Poly(butylene succinate-co-adipate) (PBSA)/poly (trimethylene carbonate) (PTMC) blend samples with different weight ratios were prepared by solution blending. The morphologies after isothermal crystallization and in the melt were observed by optical microscopy (OM). Differential scanning calorimetry (DSC) was used to characterize the isothermal crystallization kinetics and melting behaviors. According to the OM image before and after melting, it was found that the blends formed heterogenous morphologies. When the PTMC content was low (20%), PBSA formed the continuous phase, while when the PTMC contents was high (40%), PBSA formed the dispersed phase. The glass transition temperatures (T-g) of the blends were determined by DSC and the differences of the T-g values were smaller than the difference between those of pure PBSA and PTMC. In addition, the equilibrium melting points were depressed in the blends. According to these results, the PBSA/PTMC blends were determined as being partially miscible blends. The crystallization kinetics was investigated according to the Avrami equation. It was found that the incorporation of PTMC did not change the crystallization mechanism of PBSA. However, the crystallization rate decreased with the increase of PTMC contents. The change of crystallization kinetics is related with the existences of amorphous PTMC, the partial miscibility between PLLA and PTMC, and the changes of phase structures.

• 出版日期2016
• 单位山东科技大学