Novel microwave assisted chemical synthesis of Nd2Fe14B hard magnetic nanoparticles

作者：Swaminathan Viswanathan; Deheri Pratap Kumar; Bhame Shekhar Dnyaneswar; Ramanujan Raju Vijayaraghavan^*

来源：Nanoscale, 2013, 5(7): 2718-2725.

DOI：10.1039/c3nr33296a

The high coercivity and excellent energy product of Nd2Fe14B hard magnets have led to a large number of high value added industrial applications. Chemical synthesis of Nd2Fe14B nanoparticles is challenging due to the large reduction potential of Nd3+ and the high tendency for Nd2Fe14B oxidation. We report the novel synthesis of Nd2Fe14B nanoparticles by a microwave assisted combustion process. The process consisted of Nd-Fe-B mixed oxide preparation by microwave assisted combustion, followed by the reduction of the mixed oxide by CaH2. This combustion process is fast, energy efficient and offers facile elemental substitution. The coercivity of the resulting powders was similar to 8.0 kOe and the saturation magnetization was similar to 40 emu g(-1). After removal of CaO by washing, saturation magnetization increased and an energy product of 3.57 MGOe was obtained. A range of magnetic properties was obtained by varying the microwave power, reduction temperature and Nd to Fe ratio. A transition from soft to exchange coupled to hard magnetic properties was obtained by varying the composition of NdxFe1-xB8 (x varies from 7% to 40%). This synthesis procedure offers an inexpensive and facile platform to produce exchange coupled hard magnets.

• 出版日期2013
• 单位南阳理工学院