Analysis of the Plasticity-Enhancing Mechanisms in 12 pctMn Austeno-ferritic Steel by In Situ Neutron Diffraction

作者：Lee Sangwon^*; Woo Wanchuck; Decooman Bruno C

来源：Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 2014, 45A(13): 5823-5828.

DOI：10.1007/s11661-014-2593-6

The tensile behavior of ductile ultra-high strength Fe-12 pctMn-0.3 pctC-2 pctAl austeno-ferritic steel was studied by in situ neutron diffraction measurement of the elastic lattice strains, dislocation density, stacking fault probability, and strain-induced transformation kinetics. Micro-yielding was observed in austenite, and the plastic deformation of ferrite remained very limited throughout the deformation. The analysis identified three contributions to the strain hardening: twinning-induced plasticity, transformation-induced plasticity, and the accumulation of a high density of geometrically necessary dislocations accommodating the strain mismatch at the phase boundaries.