An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on silicon microwires for photoelectrochemical hydrogen evolution

作者：Chen, Chih-Jung; Chen, Po-Tzu; Basu, Mrinmoyee; Yang, Kai-Chih; Lu, Ying-Rui; Dong, Chung-Li; Ma, Chong-Geng; Shen, Chin-Chang; Hu, Shu-Fen; Liu, Ru-Shi

来源：Journal of Materials Chemistry A, 2015, 3(46): 23466-23476.

DOI：10.1039/c5ta06202k

• SULFIDE CATALYST
• H-2 EVOLUTION
• WATER
• GENERATION
• PHOTOCATHODE
• EFFICIENT
• SI
• PERFORMANCE
• NANOWIRES
• NI

An integrated cobalt disulfide (CoS2) co-catalyst passivation layer on Si microwires (MWs) was used as a photocathode for solar hydrogen evolution. Si MWs were prepared by photolithography and dry etching techniques. The CoS2Si photocathodes were subsequently prepared by chemical deposition and thermal sulfidation of the Co(OH)(2) outer shell. The optimized onset potential and photocurrent of the CoS2Si electrode were 0.248 V and -3.22 mA cm(-2) (at 0 V), respectively. The best photocatalytic activity of the CoS2Si electrode resulted from lower charge transfer resistances among the photoabsorber, co-catalyst, and redox couples in the electrolyte. X-ray absorption near edge structure was conducted to investigate the unoccupied electronic states of the CoS2 layer. We propose that more vacancies in the S-3p unoccupied states of the CoS2Si electrode were present with a lower negative charge of S-2(2-) to form weaker S-H bond strength, promoting water splitting efficiency. Moreover, the CoS2 co-catalyst that completely covered underlying Si MWs served as a passivation layer to prevent oxidation and reduce degradation during photoelectrochemical measurements. Therefore, the optimal CoS2Si electrode maintained the photocurrent at about -3 mA cm-2 (at 0 V) for 9 h, and its hydrogen generation rate was approximately 0.833 mu mol min(-1).

• 出版日期2015
• 单位重庆邮电大学