科研之友
微信
新浪微博
Facebook
分享链接
摘要
In this study, the assimilation behaviors between calcium ferrite (CF), calcium diferrite (CF2) and sintered Al2O3, and MgO were explored by an improved sessile drop technique, and the interfacial microstructure was discussed. The results indicated that the apparent contact angles of CF slag on Al2O3 and MgO substrate were 15.7 and 5.5 deg, and the apparent contact angles of CF2 slag on Al2O3 and MgO substrate were 17.9 and 7.2 deg, respectively. Namely, CF and CF2 slag were wetting well with Al2O3 and MgO substrate. The dissolution of Al2O3 substrate into the CF and CF2 slag was found to be the driving force of the wetting process. For the CF-MgO and CF2-MgO substrate systems, CaO contrarily distributed with MgO after wetting. For the CF-MgO system, after wetting, the slag was composed of CF and C2F, and most of the Fe2O3 permeated into substrate and formed two permeating layers.
