Ag-Al2O3 catalysts for lean NOx reduction-Influence of preparation method and reductant

作者：Kannisto Hannes^*; Ingelsten Hanna Harelind; Skoglundh Magnus

来源：Journal of Molecular Catalysis A: Chemical , 2009, 302(1-2): 86-96.

DOI：10.1016/j.molcata.2008.12.003

• Lean NOx reduction
• Ag
• Al2O3
• Impregnation
• Sol-gel

Alumina supported silver catalysts for selective catalytic reduction of NOx with hydrocarbons under excess oxygen (HC-SCR) were prepared according to three different methods. These are impregnation (I) and two different sol-gel routes, via thermal drying (II) or freeze-drying (III). The latter method has not previously been reported for preparation of Ag-Al2O3 catalysts. The prepared samples were characterized by N-2-sorption, TEM, XRD and XPS, and the catalytic properties were further investigated in flow reactor experiments. Two different hydrocarbons (propene and n-octane) were used separately as reductants for the SCR reaction. The TEM, XRD and XPS analyses confirmed that the sol-gel samples contain more dispersed silver of higher oxidation state than the corresponding impregnated sample. Further, it was shown that the freeze-dried sol-gel samples most likely contain well dispersed silver throughout the alumina matrix, mainly as oxidized silver. The XPS results also strongly indicate the presence of silver clusters on the surface of samples prepared by routes (I) and (II). The results from the flow reactor study imply that the ratio between silver clusters and oxidized silver species is crucial to achieve high NO reduction.

• 出版日期2009-4-1