Miniemulsion vs. conventional emulsion polymerization for pressure-sensitive adhesives production

作者：Fonseca Gabriela E; McKenna Timothy F; Dube Marc A^*

来源：Chemical Engineering Science, 2010, 65(9): 2797-2810.

DOI：10.1016/j.ces.2010.01.017

• Emulsion
• Polymerization
• Viscoelasticity
• Microstructure
• Particle formation
• Pressure sensitive adhesive

A systematic study of the production of poly(2-ethyl hexyl acrylate/methyl methacrylate/acrylic acid) pressure-sensitive adhesives (PSAs) via conventional emulsion and miniemulsion polymerization was carried out in order to discern and compare the influence of copolymer composition, chain transfer agent (CTA) and surfactant concentrations on the kinetics and microstructure of the resulting adhesive films. The results showed that miniemulsion polymerization proceeded solely under droplet nucleation for a certain set of initial reaction conditions. The miniemulsion-based latexes presented a polymer microstructure that was different to that found in latexes produced by conventional emulsion polymerization, as observed in the frequency master curves and PSA performance analysis. Batch miniemulsion polymerization was able to produce films with entanglement densities (M(w)/M(e)) from 2 up to 11, which were strongly correlated with loop tack, peel strength and shear strength. Conversely, under the same reaction conditions, batch conventional emulsion polymerization was only able to produce M(w)/M(e) ratios below 2.

• 出版日期2010-5-1