Scanning electron microscopy of the surfaces of ion implanted SiC

作者：Malherbe Johan B^*; van der Berg N G; Kuhudzai R J; Hlatshwayo T T; Thabethe T T; Odutemowo O S; Theron C C; Friedland E; Botha A J; Wendler E

来源：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms , 2015, 354: 23-27.

DOI：10.1016/j.nimb.2015.01.045

• Nuclear materials
• SiC
• SEM
• Ion bombardment
• Microstructure

This paper gives a brief review of radiation damage-caused by particle (ions and neutrons) bombardment in SiC at different temperatures, and its annealing, with an expanded discussion on the effects occurring on the surface. The surface effects were observed using SEM (scanning electron microscopy) with an inlens detector and EBSD (electron backscatter diffraction). Two substrates were used, viz, single crystalline 6H-SiC wafers and polycrystalline SiC, where the majority of the crystallites were 3C-SiC. The surface modification of the SiC samples by 360 keV ion bombardment was studied at temperatures below (i.e. room temperature), just at (i.e. 350 degrees C), or above (i.e. 600 degrees C) the critical temperature for amorphization of SiC. For bombardment at a temperature at about the critical temperature an extra step, viz, post-bombardment annealing, was needed to ascertain the microstructure of bombarded layer. Another aspect investigated was the effect of annealing of samples with an ion bombardment-induced amorphous layer on a 6H-SiC substrate. SEM could detect that this layer started to crystalize at 900 degrees C. The resulting topography exhibited a dependence on the ion species. EBSD showed that the crystallites forming in the amorphized layer were 3C-SiC and not 6H-SiC as the substrate. The investigations also pointed out the behaviour of the epitaxial regrowth of the amorphous layer from the 6H-SiC interface.

• 出版日期2015-7-1