Ductility enhancement and superelasticity in Fe-Ni-Co-Al-Ti-B polycrystalline alloy

作者：Lee Doyup^*; Omori Toshihiro; Kainuma Ryosuke

来源：Journal of Alloys and Compounds, 2014, 617: 120-123.

DOI：10.1016/j.jallcom.2014.07.136

• Shape memory
• Microstructure
• Precipitation
• Mechanical properties

The microstructure, martensitic transformation and superelasticity were examined in Fe-30Ni-15Co-10Al-2.5Ti-0.05B polycrystalline alloy sheets. Thermoelastic transformation was obtained in an aged specimen at 550 degrees C with the gamma (FCC) + gamma' (L1(2)) structure. Moreover, it was found that a {012}< 100 > recrystallization texture was formed and that the high fraction of low energy boundaries was increased in a 98.5% cold-rolled specimen. Suppression of brittle precipitation during aging was directly observed at those boundaries, resulting in improvement of ductility, and superelastic strain of over 4% was obtained in the polycrystalline alloy in a tensile test at room temperature.

• 出版日期2014-12-25