High frequency electromagnetic properties of interstitial-atom-modified Ce2Fe17NX and its composites

作者：Li, L. Z.; Wei, J. Z.; Xia, Y. H.; Wu, R.; Yun, C.; Yang, Y. B.; Yang, W. Y.; Du, H. L.; Han, J. Z.; Liu, S. Q.; Yang, Y. C.; Wang, C. S.^*; Yang, J. B.

来源：Applied Physics Letters, 2014, 105(2): 022902.

DOI：10.1063/1.4889806

• MICROWAVE-ABSORBING PROPERTIES
• ABSORPTION PROPERTIES
• WAVE ABSORPTION
• FERRITE
• NITRIDES

The magnetic and microwave absorption properties of the interstitial atom modified intermetallic compound Ce2Fe17NX have been investigated. The Ce2Fe17NX compound shows a planar anisotropy with saturation magnetization of 1088 kA/m at room temperature. The Ce2Fe17NX paraffin composite with a mass ratio of 1:1 exhibits a permeability of mu' = 2.7 at low frequency, together with a reflection loss of -26 dB at 6.9 GHz with a thickness of 1.5 mm and -60 dB at 2.2 GHz with a thickness of 4.0 mm. It was found that this composite increases the Snoek limit and exhibits both high working frequency and permeability due to its high saturation magnetization and high ratio of the c-axis anisotropy field to the basal plane anisotropy field. Hence, it is possible that this composite can be used as a high-performance thin layer microwave absorber.

• 出版日期2014-7-14
• 单位北京大学