Flexural properties of experimental nanofiber reinforced composite are affected by resin composition and nanofiber/resin ratio

作者：Vidotti Hugo A; Manso Adriana P; Leung Victor; do Valle Accacio L; Ko Frank; Carualho Ricardo M^*

来源：Dental Materials, 2015, 31(9): 1132-1141.

DOI：10.1016/j.dental.2015.06.018

• Nanofibers
• Electrospinning
• Polyacrylonitrile
• Resin composite
• Flexural properties

Objectives. To evaluate the influence of different resin blends concentrations and nanofibers mass ratio on flexural properties of experimental Poliacrylonitrile (PAN) nanofibers reinforced composites.
Materials and methods. Poliacrylonitrile (PAN) nanofibers mats were produced by electrospinning and characterized by tensile testing and scanning electron microscopy (SEM). Experimental resin-fiber composite beams were manufactured by infiltrating PAN nanofiber mats with varied concentrations of BisGMA-TEGDMA resin blends (BisGMA/TEGDMA: 30/70, 50/50 and 70/30 weight%). The mass ratio of fiber to resin varied from 0% to 8%. Beams were cured and stored in water at 37 degrees C. Flexural strength (FS), flexural modulus (FM) and work of fracture (WF) were evaluated by three-point bending test after 24 h storage.
Results. The tensile properties of the PAN nanofibers indicated an anisotropic behavior being always higher when tested in a direction perpendicular to the rotation of the collector drum. Except for WF, the other flexural properties (FS and FM) were always higher as the ratio of BisGMA to TEGDMA increased in the neat resin beams. The addition of different ratios of PAN fibers did not affect FS and FM of the composite beams as compared to neat resin beams (p > 0.05). However, the addition of fibers significantly increased the WF of the composite beams, and this was more evident for the blends with higher TEGDMA ratios (p < 0.05).
Significance. The inclusion of PAN nanofibers into resin blends did not negatively affect the properties of the composite and resulted in an increase in toughness that is a desirable property for a candidate material for prosthodontics application.

• 出版日期2015-9