Morphology transition of the primary silicon particles in a hypereutectic A390 alloy in high pressure die casting

作者：Wang, J.; Guo, Z.^*; Song, J. L.; Hu, W. X.; Li, J. C.; Xiong, S. M.^*

来源：Scientific Reports, 2017, 7(1): 14994.

DOI：10.1038/s41598-017-15223-w

• FE-RICH INTERMETALLICS
• SLIDING WEAR BEHAVIOR
• X-RAY TOMOGRAPHY
• AL-SI ALLOYS
• IN-SITU
• MECHANICAL-PROPERTIES
• DENDRITE MORPHOLOGY
• MICROSTRUCTURE
• SOLIDIFICATION
• GROWTH

The microstructure of a high-pressure die-cast hypereutectic A390 alloy, including PSPs, pores, alpha-Al grains and Cu-rich phases, was characterized using synchrotron X-ray tomography, together with SEM, TEM and EBSD. The Cu-rich phases exhibited a net morphology and distributed at the boundaries of the a-Al grains, which in turn surrounded the PSPs. Statistical analysis of the reconstructed 1000 PSPs showed that both equivalent diameter and shape factor of the PSPs exhibited a unimodal distribution with peaks corresponding to 25 mu m and 0.78, respectively.) PSPs morphology with multiple twinning were observed and morphological or growth transition of the PSPs from regular octahedral shape (with a shape factor of 0.85 was mainly caused by the constraint of the Cu-rich phases. In particular, the presence of the Cu-rich phases restricted the growth of the a-Al grains, inducing stress on the internal silicon particles, which caused multiple twinning occurrence with higher growth potential and consequently led to growth transitions of the PSPs.

• 出版日期2017-11-3
• 单位清华大学