A direct ethanol fuel cell (DEFC), which is less prone to ethanol crossover, is reported. The cell consists of PtRu/C catalyst as the anode, Nafion (R) 117 membrane, and Ni-Co-Fe (NCF) composite catalyst as the cathode. The NCF catalyst was synthesized by mixing Ni, Co, and Fe complexes into a polymer matrix (melamine-formaldehyde resins), followed by heating the mixture at 800 degrees C under inert atmosphere. TEM and EDX experiments suggest that the NCF catalyst has alloy structures of Ni, Co and Fe. The catalytic activity of the NCF catalyst for the oxygen reduction reaction (ORR) was compared with that of commercially available Pt/C (CAP) catalyst at different ethanol concentrations. The decrease in open circuit voltage (V-oc) of the DEFC equipped with the NCF catalysts was less than that of CAP catalyst at higher ethanol concentrations. The NCF catalyst was less prone to ethanol oxidation at cathode even when ethanol crossover occurred through the Nafion (R) 117 film, which prevents voltage drop at the cathode. However, the CAP catalyst did oxidize ethanol at the cathode and caused a decrease in voltage at higher ethanol concentrations.
- 出版日期2008-3