Scanning atmospheric plasma for ultrafast reduction of graphene oxide and fabrication of highly conductive graphene films and patterns

作者：Alotaibi Faisal; Tung Tran T; Nine Md J; Kabiri Shervin; Moussa Mahmoud; Tran Diana N H; Losic Dusan^*

来源：Carbon, 2018, 127: 113-121.

DOI：10.1016/j.carbon.2017.10.075

• Plasma
• Air-plasma
• Graphene film
• Conductive film
• Reduction of graphene oxide

A new method based on scanning atmospheric plasma for an ultrafast reduction of graphene oxide (GO) and preparation of highly conductive graphene films and patterns is presented. This simple method is shown to provide a direct and scalable fabrication of graphene films on flexible and shaped substrates with a variety of patterns for broad applications. An effective and ultrafast (similar to 60 s) reduction of GO films into highly conductive graphene films at room temperature is demonstrated by this process that is impossible to achieve by conventional wet chemical and thermal reduction process. The software controlled x-y scanning unit allows fabrication of graphene films with variety of patterns on different substrates including glass, plastic, ceramics and metals with complex shapes required for flexible and wearable electronics and devices. Characterization results confirmed that a thin transparent graphene film can be produced with a surface sheets resistance of 22 k Omega/sq at the transparency of 88%, and a thick film (similar to 25 mu m) with a sheet resistance of 186 Omega/sq. A practical application of plasma fabricated graphene films was demonstrated for a supercapacitor devices able to deliver an outstanding volumetric capacitance of 536.55 F/cm(3) at a current density of 1 A/g.

• 出版日期2018-2