New Raman-Peak at 1850 cm(-1) Observed in Multiwalled Carbon Nanotubes Produced by Hydrogen Arc Discharge

作者：Chen, B.^*; Kadowaki, Y.; Inoue, S.; Ohkohchi, M.; Zhao, X.; Ando, Y.

来源：Journal of Nanoscience and Nanotechnology, 2010, 10(6): 4038-4042.

DOI：10.1166/jnn.2010.2016

• Nanotubes and Fullerenes
• MWNTs
• Hydrogen Arc Discharge
• Raman Spectra

The new peak (near 1850 cm(-1)) assigned to carbon linear chain included in the centre of very thin innermost multiwalled carbon nanotubes (MWNTs) has been verified by Raman spectroscopy. These MWNTs were produced by dc arc discharge of pure graphite rods in pure hydrogen gas and existed in the cathode deposit. In this paper, we clarified that the new Raman-peaks could also be observed in the cathode deposit including MWNTs produced by hydrogen dc arc discharge using graphite electrode with added Y or La. By changing the quantity of addition (Y or La), dc arc current and pressure of ambient hydrogen gas, the optimum condition to get maximum intensity of the new Raman-peaks was obtained. For the case of 1 wt% La, dc 50 A, H-2 pressure of 50 Torr was found to be optimum, and the intensity of new Raman-peak was even higher than the G-band peak. For the case of 1 wt% Y, dc 50 A, H-2 pressure of 50 Torr was optimum, but the intensity of new Raman-peak was weaker than the G-band peak. Transmission electron microscopy observation revealed that the crystallinity of MWNTs produced with pure graphite rod was better than those produced with added Y or La.

• 出版日期2010-6
• 单位上海大学