Layered double hydroxide modified WO3 nanorod arrays for enhanced photoelectrochemical water splitting

作者：Fan, Xiaoli; Gao, Bin; Wang, Tao; Huang, Xianli; Gong, Hao; Xue, Hairong; Guo, Hu; Song, Li; Xia, Wei; He, Jianping^*

来源：Applied Catalysis A: General , 2016, 528: 52-58.

DOI：10.1016/j.apcata.2016.09.014

• Tungsten trioxide
• Layered double hydroxide
• Co-catalyst
• Photoelectrochemical
• Water oxidation

We synthesize hierarchical WO3@NiFe-layered double hydroxide (LDH) nanoarrays via a controllable hydrothermal process to prepare WO3 nanorod arrays followed by electrochemical deposition of layer structured NiFe-LDH. The WO3@NiFe-LDH photoanodes exhibit superior photoelectrochemical water oxidation performance with lower onset potential and higher anodic photocurrent density than that of the pristine WO3 photoanode. After decorated with the ultrathin NiFe-LDH nanofiakes with optimized content, the WO3@NiFe-LDH photoanode displays negative shifted onset potential of 0.06 V and enhanced photocurrent density as high as 1.10 mA cm(-2) at the potential of 1.20 V (vs. SCE). The promising performance is attributed to that WO3 provides superior framework of photoanodes as well as the prospective light harvesting property. What's more, the NiFe-LDH can act as an efficient oxygen evolution co-catalyst to suppress charge carriers recombination and accelerate the water oxidation kinetics. This strategy develops a fascinating cost-effective approach to promote the efficiency of water splitting.

• 出版日期2016-11-25
• 单位南京航空航天大学