摘要
Hierarchical rose-like Bi2WO6 photocatalyst was successfully synthesized through a simple hydrothermal route using thiourea and acetic acid as complexing agents. The as-synthesized product was determined as pure orthorhombic Bi2WO6 based on the results of X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) measurements. The photocatalyst had an average diameter of 2-3 mu m and it was constructed by many nanoflakes. The surfaces of these nanoflakes were coarse and had many nanocrystals on them. The hierarchical rose-like structure was formed through a typical hierarchical assembly process with the synergistic action of acetic acid and thiourea. The photocatalyst showed excellent visible-light-driven photocatalytic performance, it could decompose rhodamine B(RhB) within 50 min. This excellent performance resulted from its special microstructure and the relatively large surface area.