High capacity positive electrodes for secondary Mg-ion batteries

作者：Rasul Shahid^*; Suzuki Shinya; Yamaguchi Shu; Miyayama Masaru

来源：Electrochimica Acta, 2012, 82: 243-249.

DOI：10.1016/j.electacta.2012.03.095

• Mg-ion secondary batteries
• Birnessite-MnO2
• Hollandite-MnO2
• Positive electrode
• High energy density

Composites of layered structured Birnessite-MnO2 and tunnel structured Hollandite-MnO2 in presence of acetylene black were synthesized as positive electrode materials for rechargeable Mg-ion batteries. Reversible insertion/extraction of Mg-ion in the host structures was examined in the potential range of -1.8 to 1.0 V vs. Ag/Ag+. Results indicated that Mg-ion exchanged Birnessite/acetylene black composite showed the highest discharge capacity (109 mAh g(-1)) at 1st discharge, when compared to other microstructures of Birnessite. Meanwhile, the composite comprising of 65 wt% Hol-MnO2 and 35 wt% acetylene black showed very high insertion of Mg-ion (0.87 Mg/Mn) corresponding to discharge capacity of 475 mAh g(-1) when tested at 60 degrees C in galvanostatic mode. The layered and tunneled framework of the MnO2 was retained with minor displacive adjustments even after substantial Mg-ion insertion/extraction after several cycles. However, large specific capacity loss was observed after 20 cycles in all of the microstructures probably due to Mg-ion trapping in the host lattice. Furthermore, the effect of the cation (K+) present in the tunnel of Hollandite on Mg-ion diffusion was analyzed as well and it was concluded that tunnel cation could impede the movement of Mg-ion in host structure.

• 出版日期2012-11-1