Impact behaviors at low velocity of composite laminates reinforced with fabrics of different architectures are investigated. Unidirectional prepreg, 2D woven and 3D orthogonal fabrics, all formed of Ultrahigh Molecular Weight Polyethylene (UHMWPE) filaments, were selected as reinforcements to form composite laminates using hot pressing technology. Low velocity impact tests were conducted using a drop-weight impact equipment at the energy level of 35 J. A three-coordinate measuring device was employed to determine the volume of plastic deformation and surface dent diameter. The results show that the composite laminates of single-ply 3D orthogonal woven fabric exhibit better energy absorbed capacity and impact damage resistance as compared to those of unidirectional and 2D plain-woven fabric.
- 出版日期2013-9
- 单位天津工业大学