Understanding charge transport in non-doped pristine and surface passivated hematite (Fe2O3) nanorods under front and backside illumination in the context of light induced water splitting

作者：Bassi Prince Saurabh; Li Xianglin; Fang Yanan; Loo Joachim Say Chye; Barber James^*; Wong Lydia Helena^*

来源：Physical Chemistry Chemical Physics, 2016, 18(44): 30370-30378.

DOI：10.1039/c6cp05379c

Hematite (Fe2O3) nanorods on FTO substrates have been proven to be promising photoanodes for solar fuel production but only with high temperature thermal activation which allows diffusion of tin (Sn) ions fromFTO, eventually enhancing their conductivity. Hence, there is a trade-off between the conductivity of Fe2O3, and the degradation of FTO occurring at high annealing temperatures (>750 degrees C). Here, we present a comprehensive study on undoped Fe2O3 nanorods under front and back illumination to find the optimum annealing temperature. Bulk/surface charge transport efficiency analysis demonstratesminimum bulk recombination indicating overall high quality crystalline Fe2O3 and the preservation of FTO conductivity. Surface recombination is further improved by growing a TiOx overlayer, which improves the photocurrent density from 0.2 mA cm(-2) (backside) to 1.2 mA cm(-2) under front side and 0.8 mA cm(-2) under backside illumination. It is evident from this study that the performance of undoped and unpassivated hematite nanorods is limited by electron transport, whereas that of doped/passivated hematite nanorods is limited by hole transport.

• 出版日期2016