Degradation of guanidinium-functionalized anion exchange membrane during alkaline environment

作者：Li Weiwei; Wang Shubo; Zhang Xuefei; Wang Wenping; Xie Xiaofeng^*; Pei Pucheng

来源：International Journal of Hydrogen Energy, 2014, 39(25): 13710-13717.

DOI：10.1016/j.ijhydene.2014.03.133

• Density functional theory
• Guanidinium
• Functionalized
• Anion exchange membrane
• Fuel cell

A guanidinium-functionalized anion exchange membrane (AEM) was prepared and characterized. The AEM stability in an alkaline environment and transition structures during the degradation process were studied with DFT (density functional theory)/B3LYP method, 6-31 + G (d) basis set. Experimental results and theoretical analysis showed that the second step (Step 2') of degradation reaction was the control procedure; guanidinium cation was unstable under alkaline condition. It had lower energy barriers, which decided it was easier for the degradation reaction to occur in high pH environment. The ionic conductivity of AEM was 2.4 x 10(-2) S cm(-1) at 80 degrees C. However, the AEM soaked in 1 M NaOH solution, fragments were found after 10 days. The FTIR analysis showed that the structure of the membrane had been changed due to the attack of hydroxide ion. A new substance, tetramethylurea, had produced.

• 出版日期2014-8-22
• 单位清华大学