Microstructure, Mechanical and Corrosion Properties of Friction StirWelding High Nitrogen Martensitic Stainless Steel 30Cr15Mo1N

作者：Geng, Xin; Feng, Hao; Jiang, Zhouhua; Li, Huabing^*; Zhang, Binbin; Zhang, Shucai; Wang, Qi; Li, Jizhong

来源：Metals, 2016, 6(12): 301.

DOI：10.3390/met6120301

• high nitrogen martensitic stainless steel
• friction stir welding
• microstructure
• hardness
• corrosion properties

High nitrogen martensitic stainless steel 30Cr15Mo1N plates were successfully welded by friction stir welding (FSW) at a tool rotation speed of 300 rpm with a welding speed of 100 mm/min, using W-Re tool. The sound joint with no significant nitrogen loss was successfully produced. Microstructure, mechanical and corrosion properties of an FSW joint were investigated. The results suggest that the grain size of the stir zone (SZ) is larger than the base metal (BM) and is much larger the case in SZ-top. Some carbides and nitrides rich in chromium were found in BM while not observed in SZ. The martensitic phase in SZ could transform to austenite phase during the FSW process and the higher peak temperature, the greater degree of transformation. The hardness of SZ is significantly lower than that of the BM. An abrupt change of hardness defined as hard zone (HZ) was found in the thermo-mechanically affected zone (TMAZ) on the advancing side (AS), and the HZ is attributed to a combination result of temperature, deformation, and material flow behavior. The corrosion resistance of SZ is superior to that of BM, which can be attributed to less precipitation and lower angle boundaries (LABs). The corrosion resistance of SZ-bottom is slight higher than that of SZ-top because of the finer grained structure.

• 出版日期2016-12
• 单位东北大学