摘要
In this work, microcrystalline cellulose (MCC) was activated with ultrasonic waves. The influences of ultrasonic treatment on the changes of supramolecular structures and morphology structure were studied by WAXS and SEM. The accessibility of the MCC was characterized by water retention value (WRV) and specific surficial area. The influence of ultrasonic treatment on the reactivity of MCC was investigated through the reaction of MCC being oxidized into 2,3-diadehyde cellulose (DAC) by periodate sodium. The mechanism of the reactivity change of ultrasonically treated MCC was examined. The results showed that the degree of crystallinity of MCC decreased and the degree of polymerization showed little change after treatment with ultrasonic waves. The morphologial variation of the treated MCC was significant when compared with the untreated MCC, which contribute to the improvement of accessibility. The aldehyde content of DAC prepared from ultrasonically treated MCC was improved from 64.19 to 85.00%, indicating that the regioselective oxidation reactivity of MCC was significantly improved. The aldehyde content was found to first increase with time of ultrasonic treatment to a point, and then decrease as time progressed. In addition, the aldehyde content was found to increase with an increase in ultrasonic power.
- 出版日期2008-9-5
- 单位东北林业大学