Systematic control of the electrical conductivity of poly(3,4-ethylenedioxythiophene) via oxidative chemical vapor deposition

作者：Im Sung Gap; Gleason Karen K^*

来源：Macromolecules, 2007, 40(18): 6552-6556.

DOI：10.1021/ma0628477

Systematic variation in the electrical conductivity of poly(3,4-ethylenedioxythiophene) (PEDOT) was achieved by oxidative chemical vapor deposition (oCVD). For oCVD, both the oxidant, Fe(III)Cl-3, and 3,4-ethylenedioxythiophene (EDOT) monomer are introduced in the vapor phase. A heated crucible allows for sublimation of the oxidant directly into the reactor chamber operating at 150 mTorr. Spontaneous reaction of the oxidant with the monomer introduced though a feedback-controlled mass flow system results in the rapid (> 200 nm thick film in 30 min) formation of pi-conjugated PEDOT thin films directly onto a temperature-controlled substrate. As the substrate temperature is increased from 15 to 110 degrees C, increasing conjugation length, doping level, and electrical conductivity of the PEDOT chains are observed by UV-vis absorption spectroscopy (UV-vis), Fourier transform infrared spectroscopy (FTIR), and Raman spectroscopy. Concomitantly, the measured electrical conductivity of the PEDOT films increases systematically with an apparent activation energy of 28.2 +/- 1.1 kcal/mol.

• 出版日期2007-9-4