Acoustic emission and fatigue damage induced in plasma-sprayed hydroxyapatite coating layers

作者：Laonapakul Teerawat; Otsuka Yuichi; Nimkerdphol Achariya Rakngarm; Mutoh Yoshiharu^*

来源：Journal of the Mechanical Behavior of Biomedical Materials, 2012, 8: 123-133.

DOI：10.1016/j.jmbbm.2011.11.011

• Hydroxyapatite
• Plasma spray coating
• Fatigue
• Acoustic emission

In order to improve the adhesive strength of hydroxyapatite (HAp) coatings, grit blasting with Al2O3 powder and then wet blasting with HAp/Ti mixed powders was carried out on a commercially pure Ti (cp-Ti) substrate. Subsequently, an HAp/Ti bond coat layer and HAp top coat layer were deposited by plasma spraying. Fatigue tests of the HAp-coated specimens were carried out under four-point bending. Acoustic emission (AE) signals during the entire fatigue test were monitored to investigate the fatigue cracking behavior of the HAp-coated specimens. The HAp-coated specimens could survive up to 10(7) cycles without spallation of the HAp coating layers at the stress amplitude of 120 MPa. The HAp-coated specimens without HAp/Ti bond coat layer showed shorter fatigue life and easy crack nucleation compared to the HAp-coated specimens with HAp/Ti bond coat layer. The delamination and spallation of the HAp top coat with HAp/Ti bond coat on cp-Ti was not observed until the crack propagated into the cp-Ti during the final fracture stage of the fatigue cycle. Therefore, the HAp/Ti bond coat layer was found to greatly improve the fatigue damage resistance of the HAp coating layer. Three stages of the fatigue failure behavior of the HAp top coat with HAp/Ti bond coat on a cp-Ti substrate can be clearly estimated by the AE monitoring technique. These stages are cracks nucleating and propagating in the coating layer, cracks propagating in the substrate, and cracks propagating unstably to final fracture.

• 出版日期2012-4