Design of InAs/GaSb superlattice infrared barrier detectors

作者：Delmas M; Rossignol R; Rodriguez J B; Christol P^*

来源：Superlattices and Microstructures, 2017, 104: 402-414.

DOI：10.1016/j.spmi.2017.03.001

• InAs/GaSb superlattice
• Barrier detector
• Infrared detector
• TCAD simulation
• Dark current

Design of InAs/GaSb type-II superlattice (T2SL) infrared barrier detectors is theoretically investigated. Each part of the barrier structures is studied in order to achieve optimal device operation at 150 K and 77 K, in the midwave and longwave infrared domain, respectively. Whatever the spectral domain, nBp structure with a p-type absorbing zone and an n-type contact layer is found to be the most favourable detector architecture allowing a reduction of the dark-current associated with generation-recombination processes. The nBp structures are then compared to pin photodiodes. The MWIR nBp detector with 5 mu m cut-off wavelength can operate up to 120 K, resulting in an improvement of 20 K on the operating temperature compared to the pin device. The dark-current density of the LWIR nBp device at 77 K is expected to be as low as 3.5 x 10(-4) A/cm(2) at 50 mV reverse bias, more than one decade lower than the usual T2SL photodiode. This result, for a device having cut-off wavelength at 12 lam, is at the state of the art compared to the well-known MCT 'rule 07'.

• 出版日期2017-4